CRC ALU H.T. HIGH TEMPERATURE ALUMINIUM COATING

CRC ALU H.T. HIGH TEMPERATURE ALUMINIUM COATING

Send Inquiry

CRC ALU H.T. HIGH TEMPERATURE ALUMINIUM COATING

GENERAL DESCRIPTION

High temperature aluminium coating.

A high temperature paint based on silicone resins and active aluminium pigments.Alu H.T. is designed to build a hard lasting finish that will not burn off, chip or peel at high temperatures.
FEATURES

  • High thermal stability: resists temperatures up to 600°C.
  • Excellent coverage.
  • High durability.
  • Quick drying at room temperature.
  • Very good resistance to temperature fluctuations.
  • Good weather stability. Although some loss of gloss can be noticed after extended exposure.
  • Totally lead and chromate free.
  • No chlorinated and no aromatic solvents.
  • Aerosols use dimethylether (DME) propellant for controlled application and film properties.
APPLICATIONS
  • Stove pipes
  • Stoves
  • Heaters
  • Kilns
  • Incinerators
  • Chimneys
  • Exhaust manifolds
  • Headers
  • Engines
  • Ovens
  • Steam pipes
DIRECTIONS
  • Shake aerosol can very well for at least one minute after agitator ball is free. Stir or mix bulk product well to obtain a homogeneous dispersion. Repeat frequently while using.
  • Apply to a clean, degreased, dry surface for best results. Remove rust and scale with a wire brush.
  • Apply in light, even coats; best results are obtained with 2 lighter rather than 1 heavy coat. Additional coats can be applied after 15-30 minutes.
  • Complete curing occurs during use, typically after 1 h @ 200°C or 45 min. @ 250°C.
  • When spraying is finished, clean aerosol valve by turning can upside down and pressing button until only propellant escapes. If clogging occurs, remove button and clean orifice with fine wire.
  • Do not use on energised equipment. Use in well ventilated area.
  • A safety data sheet (MSDS) according EU directive 93/112 is available for all CRC products.
TYPICAL(*) PRODUCT DATA (without propellant)
  • Appearance : mat aluminium finish
  • Resin type : silicone
  • Pigment type : non-leafing aluminium
  • Specific gravity (@ 20°C)
    • aerosol : 0,99
    • bulk : 1,11
  • Flash point (solvents)
    • aerosol : -4°C
    • bulk : 42°C
  • Coverage (30 mm, dry)
    • aerosol : approx. 2,7 m2/can (400 ml)
    • bulk : TBD
  • Drying times
  • To touch : 15 min @ 20°C (45% RH)
  • To : 24 h @ 20°C (45% RH)
  • To complete cure : 1 h @ 200°C
  • Recommended film thickness : 25-30 µm
  • Thinner / cleaner : M.E.K., acetates
  • Dry film properties (on degreased metal)
  • Heat resistance (ASTM D-2485-68)
  • Method 1 (24 h cont.) : 600°C
  • Method 2 (cycling) : 635°C
  • Adhesion on steel (NFT 30038) : 0/1
  • Flexibility : pass (after heating to 600°C, 6 mm mandrel, visual)